“How can we mold more parts on the same equipment in less time and lower our costs?” is a standard question whose common answers include reduce cycle time and/or improve mold yield efficiency. Surface treatments have been part of this solution and in the last 10 years a new family of coatings—DLC (diamond like carbon)—has come onto the scene that demonstrates the ability to further streamline costs and increase productivity.

Most DLC coatings are produced by a high-vacuum process called PACVD (Plasma Assisted Chemical Vapor Deposition) that does not exceed 400°F and applies a 2 micron (or 0.00008”) thick uniform coating that conforms to the mold texture without distortion of the geometry or change in the texture.
The DLC coatings are primarily a:C:H and are chemically stable to either strong acids or bases. The amorphous, non-crystalline structure of DLC coatings provides good corrosion resistance for the tool base material and does not need a minimum thickness to create this corrosion protection.

The family DLC coatings are very hard—ranging between 78 to 85 Rc in hardness—because the carbon contained in the coating has both Sp3 and Sp2 structure. The very dense DLC coating has a coefficient of friction ranging from 0.05 to 0.1. For reference, Teflon is 0.02 and thin dense chrome is 0.2, as measured dry by steel ball on coated disk. The carbon-based coating also exhibits a resistance to outgassed residue buildup growth, reducing the speed by which the layer grows and lengthening the time between cleanings. In general, DLC coatings are abrasion-resistant, corrosion-resistant and possess a low coefficient of friction.

Mold Benefits
For the mold user all of these characteristics mean more uptime, corrosion protection, longer tool life, dry running and improvements to your existing tooling.

More Uptime
Because of the reduced plastic residue build up, tools stay in service three to four times longer befmatore requiring maintenance. The lower surface energy of these coatings allows for faster mold clean up during maintenance, reducing the tool out of service time by more than 50 percent. Most molders see three to five more hours of mold running time per week on the same equipment—allowing more parts to be molded on average per hour, reducing the manufacturing costs.

Corrosion Protection
Due to the chemical inertness of the DLC coating and its amorphous structure, highly corrosive plastics like PVC and Nylon can be run without rapid erosion of the mold tooling. This factor dramatically increases tool life by more than three times. The choice of which base material to use can be influenced by the need to resist corrosion rather than to reduce cycle time. By using DLC coatings, a different base material can be used that allows more efficient cycle time and protects against corrosion thereby increasing the number of molded parts produced per hour.

Longer Tool Life
Many plastics materials are processed with fillers like fiberglass, talc, mica, and color additives such as TiO2 for white pigmentation, flame and mildew retardant, which are highly abrasive and/or corrosive. These can all lead to more rapid tool wear, reducing overall tool life. DLC coatings provide a hard surface that resists abrasive wear. During tool maintenance, burnt residues are challenging to remove and maintenance personnel sometimes resort to pads and wire brushes to clean the buildup off the tool. These harsh cleaning methods can shorten tool life. The barrier that DLC coatings provide reduces plastic residue adhesion building on the tools and reduces labor needs required for removal processes.

Dry Running
The low coefficient of friction and low surface energy of DLC coatings minimizes steel’s tendency to cold weld under cycling, so no lubrication is necessary for parts like ejector pins, sleeves and other sliding, nonmolding components to produce molded parts. This makes DLC coating very useful for food & beverage and medical molding, which needs to be manufactured dry because of contamination concerns.

Improvement for Existing Tooling
Since no preheating is necessary for the coating adhesion and the process temperature does not exceed 400°F, existing tools made of standard tool steels (e.g., H13, S7 and D2) can be safely coated without loss of base hardness or dimensional changes. This is because the tempering temperature is not being exceeded. DLC coating can also be applied to aluminum and beryllium copper alloys.