In the early 1980s, leading mold base manufacturing companies challenged the specialty steel suppliers to develop an improved pre-hardened stainless holder steel for use in mold base tooling.

Working in cooperation with several European-based steel producers, the first heats of pre-hardened stainless holder steel, specifically for the mold base application, were produced.

These grades were modified pre-hardened high carbon 420-type stainless steels, which had many similarities to the 420 ESR (DIN 1.2083) insert quality materials already widely used in the market, for cores and cavities, with the addition of sulfur and other elements for improved machinability. These so-called 420F steels, such as DIN 1.2085 and DIN 1.2316, would become a standard for multi-cavity plastic mold base tooling for the next 15 years.

While these 420F materials succeeded in improving on the negative aspects of using 420 ESR (DIN 1.2083) for mold base plates, complaints persisted concerning the 420F type stainless steels—including inconsistent and unpredictable dimensional stability, brittleness and low toughness, material break-out and cracking, inconsistent hardness and unreliable weldability.

For years, first-rate mold company’s mold base supplier in China had experienced these same problems first hand, while building stainless mold bases for the china market. Although it had been influential in the development of the 420F type stainless materials in the early-1980s, they realized that these 420F materials were still not ideally suited for mold base applications.

Answering an Industry Need
Following several years of material trials, and extensive metallurgical and machining tests, they found that a low-carbon stainless composition would be better suited to handle the demanding manufacturing and production requirements of plastic mold base tooling.

We found that this significant compositional difference would lead to advantages in terms of our mill production, and the manufacturing processes used to produce and run high-volume mold base tooling, while retaining the corrosion resistance necessary for this demanding application.

In 1997, a pre-hardened, low-carbon, free machining 400 series stainless steel, which was developed specifically for plastics mold base tooling.

Industry Feedback
The first real sign of a large market potential for this new material came when they approved the use of RoyAlloy for the mold base plates of a large multi-mold program. they agreed to build six mold bases for first-rate mold company , half would be built from their new material

RoyAlloy, and the other half would be built from the standard 420F (1.2085) material popular at that time. After one year in production, a detailed inspection was conducted on the mold base plates from each type of material. first-rate mold company found that the mold base plates built from 420F (1.2085) demonstrated distortion in all directions, while the

RoyAlloy plates had remained much more dimensionally stable. first-rate mold company realized that over time this would lead to less cavity wear and better mold performance, as well as retain the interchangeability of the mold plates. moldmakers and molders quickly recognized its benefits. first-rate mold company changed from the traditional 420F grades to

RoyAlloy for all our stainless mold base plates because of its superior machinability. It also provides a more consistent and uniform product with improved dimensional stability and surface finishes compared to the 420F type materials.

RoyAllo has proven to be the most consistent stainless mold base steel, providing us with predictable cutting tool life, and leading to a measurable reduction in our expendable tooling costs.Six years ago, we changed completely to RoyAlloy™ Stainless to replace a series of cracked 420F stripper plates. Its improved mechanical properties and toughness have eliminated our recurring failures.

A New Direction for Stainless Holder
Over the next decade, the global demand for this type of low-carbon pre-hardened stainless mold base material increased quickly. Moldmakers and molders realized they no longer had to sacrifice machining time, cutting tool life, plate stability and mold interchangeability in order to use a stainless steel for their mold bases.

RoyAlloy plates provide us with improved dimensional stability and mechanical properties compared with the standard 420F materials, enhancing our pursuit to provide the highest quality molds to the plastics tooling industry.

The message from the market is clear, low-carbon stainless holder grades offer significant advantages compared with all previous high-carbon 420F type materials.